When it comes to choosing the right material for mechanical structures and spare parts, Nylon PA6 sheet stands out as one of the best options on the market today. Manufactured from 100% virgin raw materials, these plates and rods offer exceptional performance and durability, making them ideal for a variety of applications.
One of the main properties of nylon PA6 sheet is its excellent toughness even at low temperatures. This makes it the material of choice for applications where mechanically lower impact resistance is critical. Whether it's heavy machinery or precision components, nylon PA6 can withstand the harshest conditions while maintaining its exceptional strength.
Another outstanding feature of nylon PA6 sheet is its high surface hardness. This property ensures the material's wear resistance, making it ideal for parts that frequently rub or wear. Whether it is gears, bearings or sliding parts, Nylon PA6 sheet can handle it with ease, providing a longer service life for your equipment.
| Item name | Extruded Nylon PA 6 sheet/rod |
| Size | 1000*2000mm |
| Thickness | 8~100mm |
| Density | 1.14g/cm3 |
| Color | Nature |
| Sample | Free |
| Item | Nylon (PA6) sheet/rod |
| Type | Extruded |
| Thickness | 3---100mm |
| Size | 1000×2000, 610×1220mm |
| Color | White, black, blue |
| Proportion | 1.15g/cm³ |
| Heat resistance (continuous) | 85℃ |
| Heat resistance (short-term) | 160℃ |
| Melting point | 220℃ |
| Linear thermal expansion coefficient (average 23~100℃) | 90×10-6 m/(m.k) |
| Average 23--150℃ | 105×10-6 m/(m.k) |
| Flammability (UI94) | HB |
| Tensile modulus of elasticity | 3250MPa |
| Dipping into water at 23℃ for 24h | 0.86 |
| Dipping into water at 23℃ | 0.09 |
| Bending tensile stress / Tensile stress off shock | 76/- Mpa |
| Breaking tensile strain | >50% |
| Compressive stress of normal strain-1%/2% | 24/46 MPa |
| Pendulum gap impact test | 5.5 KJ/m2 |
| Rockwell hardness | M85 |
| Dielectric strength | 25 kv/mm |
| Volume resistance | 1014 Ω×cm |
| Surface resistance | 1013 Ω |
| Relative dielectric constant-100HZ/1MHz | 3.9/3.3 |
| Critical tracking index (CTI) | 600 |
| Bonding capacity | + |
| Food contact | + |
| Acid resistance | - |
| Alkali resistance | + |
| Carbonated water resistance | +/0 |
| Aromatic compound resistance | +/0 |
| Ketone resistance | + |