| Property | Unit | Value |
|---|---|---|
| Density | g/cm³ | 0.93-0.96 |
| Average molecular weight | g/mol | 3 million - 10 million |
| Tensile strength (23°C in air) | MPa | 22 |
| Breaking strength | MPa | 42 |
| Tensile strain at break | % | 600 |
| Charpy impact strength (notched) | mJ/mm² | No break |
| Ball indentation hardness | N/mm² | 42 |
| Shore D hardness | -- | 65-70 |
| Abrasion | % | 70-80, steel = 100 |
| Static Friction Coefficient | -- | ≤0.16 |
| Kinetic Friction Coefficient | -- | ≤0.10 |
| Water Absorption | -- | NIL |
| Elongation at break at 23 degrees | % | ≥300 |
| Temperature resistance | °C | -269 to +85 |
| Melt Temperature | °C | 130-140 |